| Title |
Integrated Hemicellulose Extraction and Papermaking Fiber Production from Agro-Waste Biomass |
| ID_Doc |
19174 |
| Authors |
Puitel, AC; Balan, CD; Ailiesei, GL; Dragoi, EN; Nechita, MT |
| Title |
Integrated Hemicellulose Extraction and Papermaking Fiber Production from Agro-Waste Biomass |
| Year |
2023 |
| Published |
Polymers, 15.0, 23 |
| DOI |
10.3390/polym15234597 |
| Abstract |
The present study deals with the valorization of corn stalks in an integrated processing strategy targeting two products: extracted hemicelluloses (HC) and papermaking fibers. Preliminary trials were conducted to assess the individual or the combined effects of biomass treatment on the quality of the obtained hemicelluloses and papermaking fibers. Depending on the hot alkaline extraction (HAE) conditions, the extracted HC had a xylan content between 44-63%. The xylan removal yield ranged between 19-35%. The recovery of HC from the extraction liquor and final black liquor was significantly affected by process conditions. The experimental approach continued with the study of HAE conditions on the obtained paper's mechanical properties. The optimization approach considered conserving paper strength properties while achieving an equilibrium with the highest possible HC extraction yield. The optimal values are sodium hydroxide concentration (1%), process time (33 min), and temperature (100 degrees C). The xylan content in the separated HC sample was similar to 55%. An extended extraction of HC from the resulting pulp under hot alkaline conditions with 5% NaOH was performed to prove the HC influence on paper strength. The xylan content in HC samples was 65%. The consequence of xylan content reduction in pulp leads to 30-50% mechanical strength loss. |
| Author Keywords |
corn stalks; xylan HC; papermaking pulp; hot alkaline extraction; tensile index; burst index |
| Index Keywords |
Index Keywords |
| Document Type |
Other |
| Open Access |
Open Access |
| Source |
Science Citation Index Expanded (SCI-EXPANDED) |
| EID |
WOS:001117667000001 |
| WoS Category |
Polymer Science |
| Research Area |
Polymer Science |
| PDF |
https://www.mdpi.com/2073-4360/15/23/4597/pdf?version=1701419465
|