Comparative study of alkali activated cements based on metallurgical slags, in terms of technological properties developed |
| ID_Doc |
23147 |
| Authors |
Gomez-Casero, MA; Perez-Villarejo, L; Sanchez-Soto, PJ; Eliche-Quesada, D |
| Title |
Comparative study of alkali activated cements based on metallurgical slags, in terms of technological properties developed |
| Year |
2022 |
| Published |
|
| DOI |
10.1016/j.scp.2022.100746 |
| Abstract |
In this work, an investigation on the use of two slags from different origins (electric arc furnace slag (EAFS) and copper slag (CS)) as raw materials in the manufacture of alkali-activated cements has been carried out. A comparison of the different mechanical properties developed by the alkaline activation of each raw material has been studied. Combination of 35 wt% potassium hydroxide (KOH) solution with different concentration (5, 8, 12 and 15 M) and 65 wt% potassium silicate (K2SiO3) solution was used as activating solution to manufacture alkali activated cements. The pastes were cured 24 h in a climatic chamber at 20 C at 90% of relative humidity, subsequently demoulded and cured at same condition during 1, 7, 28 and 90 days. Alkali activated materials have been characterized using Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The physical properties: bulk density, water absorption and apparent porosity, mechanical properties, flexural strength and compressive strength and thermal properties: thermal conductivity have been determined. The results indicate that two types of slags studied are a suitable source of aluminosilicates that can be activated for the manufacture of alkali-activated materials. These precursors are capable of developing high values of flexural and compressive strength and low values of thermal conductivity when optimal concentration of KOH was used. The optimal composition was developed when CS was utilized. Binders with CS and 12 M M ratio achieved compressive strength values up to 70 MPa. |
| Author Keywords |
Alkali activated cements; Steel slag; Copper slags; Circular economy |
| Index Keywords |
Index Keywords |
| Document Type |
Other |
| Open Access |
Open Access |
| Source |
Science Citation Index Expanded (SCI-EXPANDED) |
| EID |
WOS:000822942100004 |
| WoS Category |
Chemistry, Multidisciplinary; Green & Sustainable Science & Technology; Environmental Sciences |
| Research Area |
Chemistry; Science & Technology - Other Topics; Environmental Sciences & Ecology |
| PDF |
https://doi.org/10.1016/j.scp.2022.100746
|