| Title | Fabrication of Energy-Efficient Carbonate-Based Cementitious Material Using Sodium Meta-Aluminate Activated Limestone Powder |
|---|---|
| ID_Doc | 29370 |
| Authors | Wang, F; Long, GC; He, JH; Xie, YJ; Tang, Z; Zhou, X; Bai, M; Zhou, JL |
| Title | Fabrication of Energy-Efficient Carbonate-Based Cementitious Material Using Sodium Meta-Aluminate Activated Limestone Powder |
| Year | 2022 |
| Published | Acs Sustainable Chemistry & Engineering, 10.0, 20 |
| Abstract | Limestone powder (LP) and sodium meta-aluminate (SMA) were used to fabricate calcium carbonate-based cementitious material, as a solution to address the solid waste problem. The effects of SMA doses and curing conditions on the hydration properties and mechanical performance of paste were investigated. The results show that the 28-day unconfined compressive strength and flexural strength of the paste with an LP/SMA ratio of 2/1 were 49.7 and 15.9 MPa, respectively. The characterization by scanning electron microscopy, X-ray diffraction, and thermal gravimetry shows that the calcium aluminum carbonate hydroxide hydrate (CACHH) was the predominant hydrated product and had a dense layered double hydroxide structure (LDHs). The microbridge effect developed by LDHs significantly increases the flexural strength of the paste. Meanwhile, the developed paste exhibited an extremely low carbon emission and energy consumption. This study also reveals the mechanism of LP incorporated with SMA to form CACHH. Overall, this work provides an approach of high value-added utilization for LP as a binder without tedious operation, which could address carbon emission reduction and circular economy of LP. |
Similar Articles
| ID | Score | Article |
|---|---|---|
7089
|
Singh, SK; Tiwari, N; Jyoti Development of sustainable ternary cementitious binder with OPC integrating calcined clay and LF slag(2023) | |
| 15845
|
Li, YL; Yin, J; Yuan, Q; Huang, TJ; He, JG; Li, JB Fresh and hardened properties of cement paste and mortar incorporating calcined cutter soil mixing residue(2022) | |
| 27029
|
McDonald, LJ; Afzal, W; Glasser, FP Evidence of scawtite and tilleyite formation at ambient conditions in hydrated Portland cement blended with freshly-precipitated nano-size calcium carbonate to reduce greenhouse gas emissions(2022) | |
| 14507
|
Baggio, TF; Possan, E; Andrade, JJD Physical-chemical characterization of construction and demolition waste powder with thermomechanical activation for use as supplementary cementitious material(2024) | |
| 8679
|
Al-Janabi, A; Black, L; Adu-Amankwah, S Improvement of Recycled Cement Powder Characteristics from C&DWastes by Accelerated CO2 Curing and/or Heat Treatment(2024) | |
| 10796
|
Li, JW; Xu, D; Wang, XJ; Wang, K; Wang, WL Synergetic-Complementary Use of Industrial Solid Wastes to Prepare High-Performance Rapid Repair Mortar(2021) | |
| 8224
|
Salazar, AMO; Isaza, AV; Montoya, JWR; Arcila, JMM; García, MFV Upcycling Fly Ash, Red Clay Brick Waste, and Paper Sludge as Feedstock for Manufacturing a Lightweight Extruded Composite: Design and Characterization(2023)Buildings, 13.0, 9 | |
| 9681
|
Frías, M; de la Villa, RV; García, R; Martínez, S; Villar, E; Vegas, I Effect of a high content in activated carbon waste on low clinker cement microstructure and properties(2018) | |
| 27515
|
Suescum-Morales, D; Jiménez, JR; Fernández-Rodríguez, JM Use of Carbonated Water as Kneading in Mortars Made with Recycled Aggregates(2022)Materials, 15.0, 14 |